1 Tel: İnternet: VOLTATEX component-resin Açıklama VOLTATEX 4201 is a low emission, environmentally friendly, yellowish 1K dip resin based on unsaturated polyesterimide resins. Özellikler Once cured VOLTATEX 4201 provides a tough-hard dip resin, with low susceptibility to cracking, excellent adhesion, good elasticity and high thermo-mechanical resistance, even when subjected to extreme substained loading. The cured resin has good high long-term thermal resistance. It is very economical due to the more favourable curing conditions even at low temperatures and excellent impregnating results with low material usage. Uygulama Alanı Suitable for: - electric motors, also large-scale machines - rotors - transformers, especially heavy-duty and strip wire windings Standartlar Insulating systems up to class H acc. to IEC 85 Temperature index acc. to IEC : type 180 UL approved, file no.: E (m) RoHS compliant according to 2011/65 EC UL approved: with enamelled Cu wire: Temperature class according to UL 1446 Twisted pair ASTM D2307 Helical Coil ASTM D 2519 MW 30: 200 MW 35: 220 MW 20: 240 MW 35: 220 Electrical insulation systems according to UL 1446 class 130, 155, 180 E (Synflex system) Güncelleme 09/16-1 -

2 Tel: İnternet: Sertleştirme To achieve low hardening losses it is advisable to quickly heat up the impregnated objects to the selected curing temperature. In the case of curing processes in a drying oven, the freshair infeed should be reduced to the smallest possible amount stipulated for safety reasons. Curing times 1) at 130 C 2h at 150 C 1 h Güvenlik önlemleri Cured VOLTATEX 4201 is biologically inactive and safe to health. Implement normal protective measures when processing the liquid dip resin: See the Axalta EC safety data sheet and the M 023 data sheet of the German Chemical Industry Association (BG Chemie). Ekipmanın temizlenmesi Since the cured dip resin is practically insoluble, the tools have to be cleaned as soon as possible with Electro Cleaner E The maintenance and care of impregnating plants, especially cleaning, must be carried out according to operational requirements. Always refer to the user manual of the plant. Teslimat Şekli Dip resin VOLTATEX 4201 is delivered in 25 kg disposable containers. Depolama The resin can be stored for up to 6 months at max. 25 C if sealed correctly in original containers. Opened containers have to be resealed and protected against direct sunlight! İşleme Once cured VOLTATEX 4201 provides a tough-hard dip resin with low susceptibility to cracking, excellent adhesion, good elasticity and high thermo-mechanical resistance, even when subjected to extreme sustained loading. The cured resin has high long-term thermal resistance. It is very economical due to the more favourable curing conditions even at low temperature and excellent impregnating results with low material usage. Güncelleme 09/16-2 -

3 VOLTATEX component-resin Teknik Veriler Mekaniksel Oda sıcaklığındaki bükümlü bobinin bükülme mukavemeti mukavemeti 130 C mukavemeti 155 C mukavemeti 180 C Shore- D- sertlik oda sıcaklığında (240 ± 30) N IEC Prüfverfahren A nach IEC (90 ± 10) N IEC Prüfverfahren A nach IEC (80 ± 10 ) N IEC Prüfverfahren A nach IEC (70 ± 10 ) N IEC Prüfverfahren A nach IEC (78 ± 5) IEC Prüfverfahren nach ISO 868 Termal Sıcaklık endeksi Typ 220 IEC Prüfverfahren nach IEC Bağlama kuvveti IEC MW 30:238 C IEC, Methode B, Endpunkt 22 N Bağlama kuvveti IEC MW 35:229 C IEC, Methode B, Endpunkt 22 N Test voltajı IEC MW 30:212 C IEC Test voltajı IEC MW 35:222 C IEC Isı iletkenliği 0,23 W(m*K)- 1 angelehnt an DIN Kimyasal Birim Conditions Value Test method Dayanıklılık Verhalten gegen flüssige Beständig gegen Trafoöl, IEC , Prüfverfahren Chemiekalien destilliertes Wasser, nach ISO 175 Seifenflocken-lösung 5 %ig Güncelleme 09/16-3 -

4 Birim Conditions Value Test method Kimyasal Dayanıklılık Kältemittel / Kaltemaschinenölsystem R22 Shell UL Birim Sıvı faz Viskozite (900 ± 200 mpa s) bei 25 C nach DIN Reaksiyon seyri bei 100 C nach DuPont Werknorm 001 1) Jelleşme süresi min 8,7 Reaksiyon zamanı min 9,9 Emaye teller 3)' e etkileri Verträglich mit gebräuchlichen Lackdrähten Maksimum ısı C (175 ± 25) C 3) Elektriksel 23 C ve % 50 r.f/f.h dielektrik kuvveti kv/mm 80 kv/mm IEC Prüfverfahren nach IEC 155 C 'de dielektrik kuvveti kv/mm 80 kv/mm IEC Prüfverfahren nach IEC 96 saat %92 r.h.'da bekletildikten sonra 23 C'de dielektrik kuvveti 168 saat yağ içinde bekletildikten sonra 105 C'de dielektrik kuvveti Özgül hacim direnci 23 C özel olarak Özgül hacim direnci 155 C özel olarak kv/mm 80 kv/mm IEC Prüfverfahren nach IEC kv/mm 90kV/mm IEC Prüfverfahren nach IEC Ω*cm Ω*cm nach IEC Prüfverfahren nach IEC Ω*cm Ω*cm nach IEC Prüfverfahren nach IEC Güncelleme 09/16-4 -

5 Elektriksel Sızıntı dayanıklılığı CTI 300 M - 0,53 nach IEC Prüfverfahren nach 6.2 IEC C'de dielektrik sayısı 50 Hz ile 1 MHz arası (4,0 ± 0,5) nach EC Prüfverfahren nach IEC Zarar faktörü 23 C 30x10-3 IEC Prüfverfahren nach IEC zwischen 50 Hz und 1 MHz Zarar faktörü kesişme noktası 0,2 = 200 * C Güncelleme 09/16-5 -