Tel: +90 216 4159797 İnternet: www.synflex.com.tr VOLTATEX 4201 1-component-resin Açıklama VOLTATEX 4201 is a low emission, environmentally friendly, yellowish 1K dip resin based on unsaturated polyesterimide resins. Özellikler Once cured VOLTATEX 4201 provides a tough-hard dip resin, with low susceptibility to cracking, excellent adhesion, good elasticity and high thermo-mechanical resistance, even when subjected to extreme substained loading. The cured resin has good high long-term thermal resistance. It is very economical due to the more favourable curing conditions even at low temperatures and excellent impregnating results with low material usage. Uygulama Alanı Suitable for: - electric motors, also large-scale machines - rotors - transformers, especially heavy-duty and strip wire windings Standartlar Insulating systems up to class H acc. to IEC 85 Temperature index acc. to IEC 60455-3-5: type 180 UL approved, file no.: E 101752 (m) RoHS compliant according to 2011/65 EC UL approved: with enamelled Cu wire: Temperature class according to UL 1446 Twisted pair ASTM D2307 Helical Coil ASTM D 2519 MW 30: 200 MW 35: 220 MW 20: 240 MW 35: 220 Electrical insulation systems according to UL 1446 class 130, 155, 180 E 247773 (Synflex system) Güncelleme 09/16-1 -
Tel: +90 216 4159797 İnternet: www.synflex.com.tr Sertleştirme To achieve low hardening losses it is advisable to quickly heat up the impregnated objects to the selected curing temperature. In the case of curing processes in a drying oven, the freshair infeed should be reduced to the smallest possible amount stipulated for safety reasons. Curing times 1) at 130 C 2h at 150 C 1 h Güvenlik önlemleri Cured VOLTATEX 4201 is biologically inactive and safe to health. Implement normal protective measures when processing the liquid dip resin: See the Axalta EC safety data sheet and the M 023 data sheet of the German Chemical Industry Association (BG Chemie). Ekipmanın temizlenmesi Since the cured dip resin is practically insoluble, the tools have to be cleaned as soon as possible with Electro Cleaner E 5010. The maintenance and care of impregnating plants, especially cleaning, must be carried out according to operational requirements. Always refer to the user manual of the plant. Teslimat Şekli Dip resin VOLTATEX 4201 is delivered in 25 kg disposable containers. Depolama The resin can be stored for up to 6 months at max. 25 C if sealed correctly in original containers. Opened containers have to be resealed and protected against direct sunlight! İşleme Once cured VOLTATEX 4201 provides a tough-hard dip resin with low susceptibility to cracking, excellent adhesion, good elasticity and high thermo-mechanical resistance, even when subjected to extreme sustained loading. The cured resin has high long-term thermal resistance. It is very economical due to the more favourable curing conditions even at low temperature and excellent impregnating results with low material usage. Güncelleme 09/16-2 -
VOLTATEX 4201 1-component-resin Teknik Veriler Mekaniksel Oda sıcaklığındaki bükümlü bobinin bükülme mukavemeti mukavemeti 130 C mukavemeti 155 C mukavemeti 180 C Shore- D- sertlik oda sıcaklığında (240 ± 30) N IEC 60455-2 Prüfverfahren A nach IEC (90 ± 10) N IEC 60455-2 Prüfverfahren A nach IEC (80 ± 10 ) N IEC 60455-2 Prüfverfahren A nach IEC (70 ± 10 ) N IEC 60455-2 Prüfverfahren A nach IEC (78 ± 5) IEC 60455-2 Prüfverfahren nach ISO 868 Termal Sıcaklık endeksi Typ 220 IEC 60455-3-5 Prüfverfahren nach IEC 60216 Bağlama kuvveti IEC 60317-8 MW 30:238 C IEC, Methode B, Endpunkt 22 N Bağlama kuvveti IEC 60317-13 MW 35:229 C IEC, Methode B, Endpunkt 22 N Test voltajı IEC 60317-8 MW 30:212 C IEC 60172 Test voltajı IEC 60317-13 MW 35:222 C IEC 60172 Isı iletkenliği 0,23 W(m*K)- 1 angelehnt an DIN 501046 Kimyasal Birim Conditions Value Test method Dayanıklılık Verhalten gegen flüssige Beständig gegen Trafoöl, IEC 60455-2, Prüfverfahren Chemiekalien destilliertes Wasser, nach ISO 175 Seifenflocken-lösung 5 %ig Güncelleme 09/16-3 -
Birim Conditions Value Test method Kimyasal Dayanıklılık Kältemittel / Kaltemaschinenölsystem R22 Shell 22-12 UL 984-41 Birim Sıvı faz Viskozite (900 ± 200 mpa s) bei 25 C nach DIN 53019 Reaksiyon seyri bei 100 C nach DuPont Werknorm 001 1) Jelleşme süresi min 8,7 Reaksiyon zamanı min 9,9 Emaye teller 3)' e etkileri Verträglich mit gebräuchlichen Lackdrähten Maksimum ısı C (175 ± 25) C 3) Elektriksel 23 C ve % 50 r.f/f.h dielektrik kuvveti kv/mm 80 kv/mm IEC 60455-2 Prüfverfahren nach IEC 155 C 'de dielektrik kuvveti kv/mm 80 kv/mm IEC 60455-2 Prüfverfahren nach IEC 96 saat %92 r.h.'da bekletildikten sonra 23 C'de dielektrik kuvveti 168 saat yağ içinde bekletildikten sonra 105 C'de dielektrik kuvveti Özgül hacim direnci 23 C özel olarak Özgül hacim direnci 155 C özel olarak kv/mm 80 kv/mm IEC 60455-2 Prüfverfahren nach IEC kv/mm 90kV/mm IEC 60455-2 Prüfverfahren nach IEC Ω*cm 10 15 Ω*cm nach IEC 60455-2 Prüfverfahren nach IEC 60093 Ω*cm 10 10 Ω*cm nach IEC 60455-2 Prüfverfahren nach IEC 60093 Güncelleme 09/16-4 -
Elektriksel Sızıntı dayanıklılığı CTI 300 M - 0,53 nach IEC 60455-2 Prüfverfahren nach 6.2 IEC 60112 23 C'de dielektrik sayısı 50 Hz ile 1 MHz arası (4,0 ± 0,5) nach EC 60455-2 Prüfverfahren nach IEC 60250 Zarar faktörü 23 C 30x10-3 IEC 60455-2 Prüfverfahren nach IEC 60250 zwischen 50 Hz und 1 MHz Zarar faktörü kesişme noktası 0,2 = 200 * 10-3 135 C Güncelleme 09/16-5 -